Data Tables
Famoronana simika:
2205 Stainless vy coiled fantsona simika composition
| Cr | Ni | Mo | Co | Nb (+Ta) | Ti | V | W | Cu | C | Mn | N | Si | P | S | Fe | Al | |
| Min | 22.00 | 4.50 | 3.00 | 0.14 | 0.20 | ||||||||||||
| Max | 23.00 | 6.50 | 3.50 | 0.03 | 0.20 | 0.70 | 0.03 | 0.02 | Bal |
Toetra mekanika:
2205 Stainless vy coiled fantsona simika composition
| 0,2% ny adin-tsaina | 450 N/mm2 | 65ksi |
| Faharetana amin'ny sintona | 655 N/mm2 | 95ksi |
| Elongation, 5.65√S0 | 25% | |
| Fampihenana ny faritra | 45% | |
| Hardness (Brinell) | <270 | |
| Herin'ny fiatraikany (Temp-efitrano) | 80J (av) | |
| Herin'ny fiantraika (-46°C) : Lava | <100mm 80J | |
| 100-260mm 45J (35J min) | ||
| >260mm Raha mila fanazavana fotsiny | ||
| Herin'ny fiantraikany (-46oC): Mivadika | 50-260mm 45J (35J min) | |
| >260mm Raha mila fanazavana fotsiny | ||
Fanamarihana:
2205 Stainless vy coiled fantsona simika composition
- Ny fitsapana dia atao mifanaraka amin'ny ASTM A370 na EN ISO 6892-1 (tensile), EN ISO 6506-1 (hardness)
- Toerana faran'izay kely voatonona (voasedra amin'ny mari-pana amin'ny efitra mizotra amin'ny lalana lava)
- Fitsapana natao isaky ny mitsonika ny akora isaky ny andiany fitsaboana hafanana
- Ny hamafin'ny dia tokony hifanaraka amin'ny NACE MR 1075
- ASTM G48A corrosion test (amin'ny 25°C) Tsy misy pitting ary <3.0g/m2lanja very
- Ny votoatin'ny ferrite 40-55%
- Ny microstructure voamarina tsy misy karbida sisintany voamaina, sigma, chi ary laves
Toetra ara-batana: 2205 stainless vy coiled tube simika composition
| Hateza (Kg/m3) | 7810 |
| Fahavitrihana andriamby (20°C) | <50 |
| Ny Modulus Young (kN/mm2) | 190 |
| Fanoherana herinaratra manokana, 20°C (µΩ.m) | 0.85 |
| Ny salan'isa amin'ny fanitarana mafana, 20-300°C (m/m/oC) | 11 x 10-6 |
| Hafanana manokana, 20°C (J/kg.K) | 400 |
| Conductivity mafana, 20°C (W/mK) |
Fotoana fandefasana: May-25-2023